ANYCUBIC Water-Wash Resin 3D Printers Resin Water-Washable 365-405nm for LCD DLP

🔥 All are ready stock in Sungai besi office & ship within 24 hours* (Except for non working day, but do call us to check)

🔥 Select Others (West Malaysia) as shipment if you’d like to opt for self-pickup/by delivery services (Lalamove, Grab, etc ). Contact us after placed order.etc )

Anycubic Water Washable + is an upgrade resin which greatly REDUCE CRACK attacked by water especially during cleaning or the print that put at high moisture level environment.

Features:

[Super Easy to Clean]

Contains hydrophilic groups with good water solubility, which is can be directly cleaned with water instead of alcohol and greatly save the cost of alcohol use.

[High Precision and Low Shrinkage]

Low shrinkage during the photo curing process, which ensures the high precision and smooth surface. The low shrinkage rate ensures that every model is printed in good details.

[Low Odor and Sage]

Low odor and it can ensure customers with a better printing experience. Take a full shake before use in order to have a fully mix the functional components and fully mix the color paste in the resin. Otherwise, uneven coloring of the print may occur.

[Low Viscosity and Good Fluidity]

Low resin viscosity means good fluidity in the printing process, which greatly improves the printing success rate. Anycubic upgraded water washable resin has a longer shelf life to 1 and a half years to help the resin to store longer and safe use.

[Wide Compatibility]

Compatible with 365-405nm wide band, Anycubic resin is suitable for most 3D LCD DLP printers on the market, better effect with ANYCUBIC LCD 3D printers.

*It is not recommended to pour the cleaning waste liquid directly into the sewer. It is recommended that the residual resin be treated by light curing after outdoor evaporation or heating to evaporate the water.

Specification:

Wavelength: 365-405nm

Density: 1.15-1.2 g/cm³

Viscosity: 150-250 cP or mPa·s

Surface hardness: 80HD

Tensile strength: 30-45 MPa

Elongation at break: 8%-15%

Molding shrinkage: 3.72%-4.24%

Flexural strength: 50-60 MPa

Flexural modulus: 1500-1600 MPa

Shelf life: 1.5 years